Aim: This study aimed to assess the prevalence of temporomandibular disorders (TMD) and psychosocial comorbidities in undergraduate dental students in a southern Brazilian university, during the COVID-19 pandemic. Also, it aimed to verify the association between psychosocial factors and TMD. Methods: Fonseca Anamnestic Index, Depression Anxiety Stress Scale (DASS-21), a socioeconomic questionnaire, and questions about academic performance and social distancing were applied. Poisson regression analysis was used to assess the association of predictive variables with TMD. Results: The prevalence of TMD was found to be 82.4%, and more than half of the students had some degree of stress, anxiety, and depression. Students who had symptoms of stress (RR 1.11; 95% CI 1.04-1.19), anxiety (RR 1.19; 95% CI 1.12-1.27) and reported academic performance worsening (RR 1.12; 95% CI 1.07-1.19) had higher TMD scores. Conclusion: The findings suggest that TMD was highly prevalent among dental students at a federal university in southern Brazil during the pandemic, being associated with high levels of stress, anxiety, poor academic performance, and greater social distancing

Effect of intrinsic pigmentation on the flexural strength of a microwave-cured acrylic resin

This study investigated the effect of intrinsic pigmentation on the transverse strength of a microwave-cured acrylic resin. Forty transverse strength specimens were fabricated according to ADA specification #12 and divided into 5 groups. No fibers were added to group I (GI, control group); acrylic stain (AS) was added to GII and GIII in concentrations of 0.5 and 1.5 percent w/w, respectively; acrylic fibers (AF) were added to groups GIV and GV in concentrations of 0.5 and 1.5 percent w/w, respectively. All specimens were irradiated in a microwave oven with a cycle of 3 min at 360 W, followed by 4 min resting, then 3 min at 810 W. Flasks were bench-cooled for 30 min at room temperature, followed by immersion in cold tap water for 30 min. After storage in distilled water at 37ºC for 48 h, all specimens were tested for flexural strength in a testing machine (EMIC-DL 500) at a crosshead speed of 0.5 cm/min. Mean and standard deviation (MPa) for the flexural strength test were: GI=86.0 ± 7.9; GII=86.0 ± 9.8; GIII=86.6 ± 7.7; GIV=84.9 ± 5.3; GV=84.9 ± 5.2. No statistical differences were detected among the groups (ANOVA, p>0.05). The addition of the acrylic fibers or the acrylic stain did not affect the transverse strength of the microwave-cured acrylic resin

Técnica de caracterizaçäo de bases de prótese utilizando fibras de lä acrílica / Denture bases characterization technique using acrylic wool fibers

Os autores apresentam uma técnica de pigmentaçäo intrínseca de bases de prótese através da incorporaçäo em camadas de fios de lä acrílica na resina de cura térmica. O método de caracterizaçäo utilizado reproduz a translucidez, a profundidade e os tons dos tecidos gengivais, tornando a base da prótese mais natural